Products for Coatings used in Transportation (Resins & Systems)
| Product Name & Description | Category | Type | EEW Based on solids (g/eq) | AHEW Based on solids (g/eg) | Viscosity @25°C (mPa.s) | Softening Point | Solids Content (wt%) | Regional Availability
APAC - Asia, Pacific
EMEAI - Europe, Middle East, Africa, India LAA - Latin America Area NAA - North America Area |
Footnote |
|---|---|---|---|---|---|---|---|---|---|
|
D.E.H.® 800
Polyamine adduct hardener DISSOLVED in water (storage/shear stable). Alkali-resistant so useful for ECC. Visible end of pot-life. In combination with solid epoxy emulsion suitable for corrosion protection on steel. Can be used on fresh concrete (immediately after being laid). |
Waterborne Systems | Waterborne Epoxy Curing Agents | – | 150 | 5,000 – 1,0000 | – | 50 | APAC, EMEAI, LAA, NAA | – |
|
D.E.H.® 805
Standard for Coating on Concrete. Not compatible with Zink Phosphates. Calcium phosphates could be used but more expensive. Visible end of pot-life. D.E.H. 805 allows to develop roller coat formulations with a matte, satin or high gloss finish. |
Waterborne Systems | Waterborne Epoxy Curing Agents | – | 220 | 10,000 – 19,000 | – | 65 | APAC, EMEAI, LAA, NAA | – |
|
D.E.H.® 810
Designed for best corrosion protection. Not compatible with anti-corrosion pigments (zinc-phosphates). Best for clear coatings with solid epoxy dispersions. Show excellent adhesion to diamonds (Closest we have to Waterpoxy 751). |
Waterborne Systems | Waterborne Epoxy Curing Agents | – | 150 | 2,000 – 4,000 | – | 50 | APAC, EMEAI, LAA, NAA | – |
|
D.E.H.® 813
Designed for faster curing corrosion protection, i.e. faster version of 7006. Can handle zinc phosphate (anti-corrosion pigments). NO visible end of pot life with solid epoxy resin dispersions. Should not be used in too thick layer > 300 mu otherwise “mud-cracking” can occur. Can be dust-free in 30 minutes (when formulated) |
Waterborne Systems | Waterborne Epoxy Curing Agents | – | 140 | 5,000 – 1,0000 | – | 70 | EMEAI, LAA | – |
|
D.E.H.® 820
Waterborne amine-adduct curing agent without free amine. Suitable for use in applications requiring German potable water contact certification. |
Waterborne Systems | Waterborne Epoxy Curing Agents | – | 163 | 7,000 – 17,000 | – | 65 | APAC, EMEAI, LAA | – |
|
D.E.N.® 424
Approximately 2.4 functional low viscosity liquid epoxy novolac resin. D.E.N. 424 fills the gap between the standard Bisphenol F based liquid epoxy resin and multifunctional, low viscosity epoxy novolac resin D.E.N 425. Compared to standard Bisphenol A and Bisphenol F based liquid epoxy resins, D.E.N. 424 produces an improved crosslinked system, which enables better thermal and chemical resistance with a low viscosity that is necessary for easy processing and application. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 165 – 175 | – | 5,700 – 6,800 | – | – | LAA, NAA | – |
|
D.E.N.® 425
Approximately 2.5 functional liquid epoxy novolac resin bridging between standard liquid epoxy resin and semi-solid epoxy novolac resins. When used in combination with a fast curing agent no post-cure is required and binder systems are obtained with excellent mechanical and especially solvent resistance properties. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 169 – 175 | – | 9,500 – 12,500 | – | 100 | EMEAI, LAA, NAA | – |
|
D.E.N.® 426
Approximately 2.6 functional medium viscosity liquid epoxy novolac resin. D.E.N. 426 fills the gap between lower viscosity epoxy novolac resins such as D.E.N. 424 and higher viscosity epoxy novolac resins such as D.E.N. 431 and D.E.N. 438. When using D.E.N. 426 with carefully selected curing agents, the system provides faster thin film drying time at ambient temperature and has better resistance to chemicals such as acetic acid, toluene, and methanol. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 167 – 177 | – | 18,000 – 23,000 | – | – | LAA, NAA | – |
|
D.E.N.® 428
Multi-functional (±2.8) epoxy novolac resin of lower viscosity compared to the higher viscosity epoxy novolac epoxy resin D.E.N. 431. In addition to improved processing of this medium viscosity novolac resin, D.E.N. 428 is distinguished by particularly good thermal resistance, chemical resistance, and mechanical properties. With these characteristic properties, D.E.N. 428 is suitable for applications such as protective coatings or linings for storage tanks, pipes, and pumps. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 168 – 178 | – | 35,000 – 45,000 | – | – | LAA, NAA | – |
|
D.E.N.® 431
Multi-functional (±2.8) epoxy novolac resin of lower molecular weight for application where solvents cannot be tolerated and application viscosity (temperature) needs to remain relatively low. Used in adhesives, electrical and structural laminates and castings for elevated temperature service and excellent chemical resistance. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 172 – 179 | – | 1,100 – 1,700 (1) | – | 100 | APAC, EMEAI, LAA, NAA | 1 at 51.7°C |
|
D.E.N.® 431 EK98
Solution of D.E.N. 431 in methyl-ethyl ketone® |
Epoxy Novolac Resins | Epoxy Novolac Solutions | 172 – 179 | – | 5,000 – 25,000 | – | 98 | NAA | – |
|
D.E.N.® 438®
Highly functional (±3.6) epoxy novolac resin offering best mechanical, temperature and chemical resistance performance with acceptable viscosity. Recognized as a standard for high-temperature applications. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 176 – 181 | – | 31,000 – 40,000 (1) | – | 100 | APAC, EMEAI, LAA, NAA | 1 at 51.7°C |
|
D.E.N.® 438-A85
Solution of D.E.N. 438 in acetone mainly for laminating or Prepreg applications. |
Epoxy Novolac Resins | Epoxy Novolac Solutions | 176 – 181 | – | 500 – 1,200 | – | 84 – 86 | APAC, EMEAI, LAA, NAA | – |
|
D.E.N.® 438-EK85
Solution of D.E.N. 438 in methyl-ethyl ketone mainly for laminating or Prepreg applications. |
Epoxy Novolac Resins | Epoxy Novolac Solutions | 176 – 181 | – | 600 – 1,600 | – | 84 – 86 | APAC, EMEAI, LAA, NAA | – |
|
D.E.N.® 438-MAK80
Solution of D.E.N. 438 in methyl n-amyl ketone mainly for laminating or Prepreg applications. |
Epoxy Novolac Resins | Epoxy Novolac Solutions | 176 – 181 | – | 600 – 1,200 | – | 79 – 81 | NAA | – |
|
D.E.N.® 438-MK75
Solution of D.E.N. 438 in methyl iso-butyl ketone mainly for laminating or Prepreg applications. |
Epoxy Novolac Resins | Epoxy Novolac Solutions | 176 – 181 | – | 200 – 600 | – | 74 – 76 | NAA | – |
|
D.E.N.® 438-MK80
Solution of D.E.N. 438 in methyl iso-butyl ketone mainly for laminating or Prepreg applications. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 176 – 181 | – | 800 – 1200 | – | 80 | LAA, NAA | – |
|
D.E.N.® 438-X80
Solution of D.E.N. 438 in Xylene. Main use in wet-paint systems with high temperature or chemical resistance requirements. |
Epoxy Novolac Resins | Epoxy Novolac Solutions | 176 – 181 | – | 1,200 – 2,000 | – | 79 – 81 | APAC, EMEAI, LAA, NAA | – |
|
D.E.N.® 438L
Low(er) viscosity version of D.E.N. 438 epoxy novolac resin to allow higher solids and/or lower viscosity formulations. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 176 – 181 | – | 27,500 – 32,500 (1) | – | 100 | NAA | 1 at 51.7°C |
|
D.E.N.® 439
Highly functional (±3.8) epoxy novolac resin with improved reactivity. The higher viscosity offers a means of obtaining good drape and limited tack in Prepreg formulations. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 191 – 210 | – | 15,000 – 35,000 (2) | – | 100 | APAC, EMEAI, LAA, NAA | 2 at 71°C |
|
D.E.N.® 439-EK85
Solution of D.E.N. 439 in methyl-ethyl ketone mainly for laminating or Prepreg applications. |
Epoxy Novolac Resins | Epoxy Novolac Solutions | 191 – 210 | – | 4,000 – 10,000 | – | 84 – 86 | NAA | – |
|
D.E.N.® 439-H
Highly functional epoxy novolac resin with lower processing variability. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 191 – 210 | – | 23,000 – 29,000 (2) | – | 100 | NAA | 2 at 71°C |
|
D.E.N.® 440
Extremely high functional (± 4.4) epoxy novolac resin. Offers highest performance in this product group with regards to mechanical, temperature and chemical resistance properties. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 186 – 192 | – | 20,000 – 45,000 (2) | – | 100 | EMEAI, NAA | 2 at 71°C |
|
D.E.R.® 301
Modified liquid epoxy resin; compared with standard bisphenol A based liquid epoxy resin, similar viscosity, improved flexibility, longer pot life and anticorrosion performance; suitable for high solids (80% volume solid above) formulation. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 245 – 265 | – | 10,000 – 14,000 | – | 100 | APAC | – |
|
D.E.R.® 317
High viscosity, fast reacting (20% faster than D.E.R. 331) liquid epoxy resin designed for adhesive applications requiring quick gelling with amine curing agents. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 192 – 203 | – | 16,000 – 25,000 | – | 100 | NAA | – |
|
D.E.R.® 321
Very low viscosity resin allowing large amounts of fillers. Cure rate similar to undiluted resins. Improved acid resistance can be observed. For floorings, grouting, concrete reinforcement, structural adhesives, crack injection and castings. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 180 – 188 | – | 500 – 700 | – | 100 | EMEAI, LAA, NAA | – |
|
D.E.R.® 3212
Similar to D.E.R. 321 epoxy resin but of higher viscosity maintaining more mechanical strength. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 179 – 193 | – | 750 – 1,400 | – | 100 | LAA, NAA | – |
|
D.E.R.® 322
Low diluent content resin combining significant viscosity reduction whilst maintaining mechanical strength properties. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 183 – 193 | – | 5,500 – 8,500 | – | 100 | NAA | – |
|
D.E.R.® 3221
Liquid epoxy resin especially suitable for use in water borne epoxy binder systems. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 187 – 208 | – | 700 – 1,000 | – | 100 | EMEAI | – |
|
D.E.R.® 324
Offers low viscosity and low surface tension to wet the surface better, giving better adhesion and slightly lower viscosity at any given filler loading. The diluent increases pot life, flexibility (impact resistance) and acid resistance. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 195 – 204 | – | 600 – 800 | – | 100 | APAC, EMEAI, LAA, NAA | – |
|
D.E.R.® 325
Low viscosity liquid epoxy resin with reduced surface tension. Offers excellent wetting and flow. The low diluent content is the cause of the improved mechanical properties over D.E.R. 323 and D.E.R. 324 epoxy resin. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 185 – 206 | – | 850 – 2,800 | – | 100 | NAA | – |
|
D.E.R.® 326
Low viscosity liquid epoxy resin with minimal crystallization tendency. Offers low surface tension, excellent wetting and flow. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 204 – 210 | – | 600 – 900 | – | 100 | NAA | – |
|
D.E.R.® 327
Lower viscosity and easier to handle than D.E.R. 326 with minimal crystallization tendency. Offers low surface tension, excellent wetting and flow. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 196 – 212 | – | 500 – 700 | – | 100 | LAA, NAA | – |
|
D.E.R.® 3271
Very low viscosity epoxy resin designed for mineral castings in combination with e.g. D.E.H. 2112 epoxy curing agent. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 156 – 170 | – | 250 – 450 | – | 100 | EMEAI | – |
|
D.E.R.® 3274
Bi-functional reactive diluent containing resin offering reduced viscosity whilst only affecting the mechanical and thermal properties moderately. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 160 – 180 | – | 1,300 – 1,500 | – | 100 | APAC, EMEAI, LAA | – |
|
D.E.R.® 3282
Reactive diluent containing epoxy resin offering low viscosity, good mechanical properties as well as solvent resistance. |
Liquid Epoxy Resins | Modified Bisphenol A Liquid Epoxy Resins | 173 – 183 | – | 900 – 1,100 | – | 100 | APAC, EMEAI | – |
|
D.E.R.® 330
D.E.R. 330 epoxy resin is a low viscosity bisphenol A epoxy resin commonly used in composite and casting applications. D.E.R. 330 epoxy resin frequently crystallizes at room temperature; heating to 50-55°C restores the resin to liquid state. Long-term warm storage may result in slight discoloration but does not affect the resin performance. |
Liquid Epoxy Resins | Bisphenol A Liquid Epoxy Resins | 176 – 185 | – | 7,000 – 10,000 | – | 100 | APAC, EMEAI, NAA | – |
|
D.E.R.® 330-EL
Lower viscosity bisphenol-A epoxy resin with very low hydrolysable chloride content (<100 ppm). Specifically suitable for electrical, electronic and encapsulation applications. |
Liquid Epoxy Resins | Bisphenol A Liquid Epoxy Resins | 176 – 185 | – | 7,000 – 10,000 | – | 100 | EMEAI | – |
|
D.E.R.® 331®
Industry standard bisphenol-A based liquid epoxy resin. Offers excellent mechanical, thermal and chemical resistance properties in multiple applications. Shows improved reactivity and wetting properties versus competitive alternatives. |
Liquid Epoxy Resins | Bisphenol A Liquid Epoxy Resins | 182 – 192 | – | 11,000 – 14,000 | – | 100 | APAC, EMEAI, LAA, NAA | – |
|
D.E.R.® 331-EL
Standard bisphenol-A epoxy resin with very low hydrolysable chloride content (<150 ppm). Specifically suitable for electrical, electronic and encapsulation applications. |
Liquid Epoxy Resins | Bisphenol A Liquid Epoxy Resins | 182 – 192 | – | 11,000 – 14,000 | – | 100 | EMEAI | – |
|
D.E.R.® 336
Standard liquid bisphenol-A epoxy resin of intermediate viscosity and equivalent weight with narrow specification limits. |
Liquid Epoxy Resins | Bisphenol A Liquid Epoxy Resins | 181 – 185 | – | 9,400 – 11,000 | – | 100 | EMEAI | – |
|
D.E.R.® 336-EL
Intermediate viscosity epoxy resin with very low hydrolysable chloride content (<150 ppm). Specifically suitable for electrical, electronic and encapsulation applications. |
Liquid Epoxy Resins | Bisphenol A Liquid Epoxy Resins | 181 – 185 | – | 9,400 – 11,000 | – | 100 | EMEAI | – |
|
D.E.R.® 337
Intermediate epoxy equivalent weight semi-solid epoxy resin, mainly used in adhesives and protective coatings, or as a modifier for other epoxy resins to improve impact strength, extensibility and adhesion. |
Liquid Epoxy Resins | Bisphenol A Liquid Epoxy Resins | 230 – 250 | – | 400 – 800 (1) | – | 100 | APAC, EMEAI, NAA | (1) 70 wt% in diethylene glycol monobutyl ether |
|
D.E.R.® 337-DA97
Solution of D.E.R. 337 in diacetone alcohol. |
Liquid Epoxy Resins | Epoxy Resin Solutions | 230 – 278 | – | NA | – | 96 – 98 | NAA | – |
|
D.E.R.® 337-X80
Solution of D.E.R. 337 in xylene. The excellent resistance and physical properties for epoxy coal tar combinations and higher solids content marine coatings. |
Liquid Epoxy Resins | Epoxy Resin Solutions | 230 – 260 | – | 500 – 1,200 | – | 79 – 81 | APAC, EMEAI, NAA | – |
|
D.E.R.® 337-X90
Solution of D.E.R. 337 in xylene. Higher solids content than D.E.R. 337-X80 epoxy resin solution. |
Liquid Epoxy Resins | Epoxy Resin Solutions | 230 – 250 | – | 5,000 – 15,000 | – | 89 – 91 | APAC, NAA | – |
|
D.E.R.® 338-X90
Solution of a semi-solid epoxy resin in xylene. |
Liquid Epoxy Resins | Epoxy Resin Solutions | 230 – 280 | – | 5,000 – 50,000 | – | 89 – 91 | NAA | – |
|
D.E.R.® 3401
Low viscosity rapidly reacting Bisphenol A/F epoxy resin designed for fast-curing coatings, adhesives, and mortars. It can be used as the sole epoxy or in combination with other epoxy resins. Rapid cure, return to service, Low emissions or substance of concern content, Low viscosity, Good chemical resistance |
Liquid Epoxy Resins | Modified Bisphenol A/F Liquid Epoxy Resins | 175 – 215 | – | 1,500 – 3,500 | – | 100 | NAA | – |
|
D.E.R.® 350
D.E.R. 350 is a bisphenol F epoxy resin that has a low tendency to crystallize. |
Liquid Epoxy Resins | Modified Bisphenol A/F Liquid Epoxy Resins | 165 – 174 | – | 2500 – 4500 | – | 100 | LAA, NAA | – |
|
D.E.R.® 351
D.E.R. 351 liquid epoxy resin is a low viscosity epoxy resin combining the performance properties of standard bisphenol A epoxy resin with the low viscosity of bisphenol F epoxy resin. The resin blend shows a low tendency to crystallization. Applications include solvent-free coatings, tank- and pipe-linings, concrete reinforcements and also floorings, adhesives, electrical insulation and filament winding. |
Liquid Epoxy Resins | Modified Bisphenol A/F Liquid Epoxy Resins | 169 – 181 | – | 1500 – 6500 | – | 100 | APAC, EMEAI, LAA, NAA | – |
|
D.E.R.® 352
Higher viscosity and more economic bisphenol-A/F liquid epoxy resin. Recommended base for many modified bisphenol-A/F liquid epoxy resins. |
Liquid Epoxy Resins | Bisphenol A/F Liquid Epoxy Resins | 172 – 181 | – | 5,700 – 7,700 | – | 100 | APAC, EMEAI, LAA, NAA | – |
|
D.E.R.® 353
Low viscosity epoxy resin with very low crystallization tendency. Offers low surface tension to wet the surface better, giving better adhesion. The diluent increases pot life, flexibility (impact resistance) and acid resistance. |
Liquid Epoxy Resins | Modified Bisphenol A/F Liquid Epoxy Resins | 190 – 200 | – | 800 – 1,000 | – | 100 | APAC, LAA, NAA | – |
|
D.E.R.® 3531
Low crystallization resin with low vapor pressure and hydrophobic in nature. Offers low viscosity and good wetting properties it is suitable for casting resin coatings and adhesives |
Liquid Epoxy Resins | Modified Bisphenol A/F Liquid Epoxy Resins | 183 – 199 | – | 750 – 1,150 | – | 100 | APAC, EMEAI | – |
|
D.E.R.® 3532
Low crystallization resin with low vapor pressure and hydrophobic in nature. Offers very low viscosity and good wetting properties. Similar to D.E.R. 3531 in nature. |
Liquid Epoxy Resins | Modified Bisphenol A/F Liquid Epoxy Resins | 181 – 200 | – | 500 – 900 | – | 100 | APAC, EMEAI, NAA | – |
|
D.E.R.® 3533
Low crystallization resin with low vapor pressure and hydrophobic in nature. Offers extremely low viscosity and good wetting properties. Similar to D.E.R. 3531/3532 in nature. |
Liquid Epoxy Resins | Modified Bisphenol A/F Liquid Epoxy Resins | 187 – 200 | – | 450 – 550 | – | 100 | APAC, EMEAI | – |
|
D.E.R.® 354
Unmodified bisphenol F-based epoxy resin of low viscosity. Improves crystallization resistance of other epoxy resins and gives improvement in solvent resistance. Frequently used in solvent-free coatings, floor coverings, adhesives or composite applications. |
Liquid Epoxy Resins | Bisphenol F Epoxy Resins | 167 – 174 | – | 3,400 – 4,200 | – | 100 | APAC, EMEAI, LAA, NAA | – |
|
D.E.R.® 354LV
D.E.R. 354LV Liquid Epoxy Resin is an unmodified bisphenol F based liquid, low viscosity epoxy resin. It is compatible with common epoxy resins and can be blended with them in any ratio. It achieves a high degree of cure at ambient temperatures, providing improved resistance performance against solvents compared to standard bisphenol A liquid epoxy resins. |
Liquid Epoxy Resins | Bisphenol F Epoxy Resins | 158 – 170 | – | 1300 – 3000 | – | 100 | LAA, NAA | – |
|
D.E.R.® 356
The product performance is very similar to that obtained with D.E.R. 352 Resin except that this resin will provide a more rapid cure (higher reactivity). |
Liquid Epoxy Resins | Bisphenol A/F Liquid Epoxy Resins | 176 – 183 | – | 6,500 – 8,000 | – | 100 | APAC, EMEAI, LAA | – |
|
D.E.R.® 3572
Liquid epoxy resin, modified with a di-funtional reactive diluent. Offers improved reactivity, better mechanical properties as well as solvent resistance versus mono functional aliphatic diluents. |
Liquid Epoxy Resins | Modified Bisphenol A/F Liquid Epoxy Resins | 164 – 176 | – | 600 – 900 | – | 100 | APAC, EMEAI | – |
|
D.E.R.® 3581
Liquid epoxy resin, modified with a lower vapor pressure di-functional reactive diluent. Offers improved reactivity, better mechanical properties as well as solvent resistance versus mono functional aliphatic diluents. |
Liquid Epoxy Resins | Modified Bisphenol A/F Liquid Epoxy Resins | 169 – 180 | – | 900 – 1,400 | – | 100 | APAC, EMEAI | – |
|
D.E.R.® 3680-X90(K)
Chemically modified low molecular weight epoxy resin in xylene. Offers lower viscosity allowing higher solids contents at similar corrosion protection properties. Improves lower temperature curing. |
Liquid Epoxy Resins | Epoxy Resin Solutions | 230 – 270 | – | 1,200 – 3,200 | – | 89 – 91 | APAC, EMEAI, LAA | – |
|
D.E.R.® 383
Lower viscosity bisphenol-A epoxy resin allowing the use of less diluents or more fillers in the formulation. Offers longer pot-life versus the standard resin and slightly improved resistance properties when used in heat curing (composite) applications. |
Liquid Epoxy Resins | Bisphenol A Liquid Epoxy Resins | 176 – 183 | – | 9,000 – 10,500 | – | 100 | APAC, LAA, NAA | – |
|
D.E.R.® 383-X20
Liquid reaction product of epichlorohydrin and Bisphenol A in xylene |
Liquid Epoxy Resins | Epoxy Resin Solutions | 176 – 183 | – | NA | – | 19 – 21 | NAA | – |
|
D.E.R.® 3912
D.E.R. 3912 is an aliphatic liquid epoxy resin flexibiliser for high solids or solvent-free coatings. |
Epoxy Toughening / Flexibilizing Solutions | Flexible Epoxy Resins | 550 – 650 | – | 21,000 – 29,000 | – | – | EMEAI | – |
|
D.E.R.® 3913
Flexible epoxy resin that offers high elongations at break at room temperature as well as at -20°C. Can be used with standard epoxy amine adduct curing agents for flooring formulations in (freezing-) cold areas. |
Epoxy Toughening / Flexibilizing Solutions | Flexible Epoxy Resins | 345 – 365 | – | 7,500 – 9,500 | – | – | APAC, EMEAI, LAA, NAA | – |
|
D.E.R.® 6116
Low molecular weight “1.5-type” epoxy resin offers excellent flow in standard and low temperature cure powder coating systems. Suggested in cases where D.E.R. 662E Resin does not provide adequate flow. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 520 – 560 | – | 550 – 1,000 (1) | 80 – 90 | 100 | LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 6155
Medium molecular weight “5 type” solid epoxy resin designed for powder coatings which require greater flexibility. |
Solid Epoxy Resins | Medium Molecular Weight Solid Epoxy Resin | 1,250 – 1,400 | – | 30,000 – 55,000 (1) | 105 – 125 | 100 | LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 6224
Low molecular weight “2.5-type” epoxy resin specifically designed for decorative powders coatings requiring excellent gloss and flow. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 675 – 725 | – | 1,500 – 2,500 (1) | 88 – 98 | 100 | NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 6225
Chemically modified bisphenol A solid epoxy resin for very high flow and gloss powder coating applications. Specifically suitable for thin film applications. |
Solid Epoxy Resins | Specialty Solid Epoxy Resins | 650 – 725 | – | 800 – 1,600 (1) | 87 – 95 | 100 | LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 6330-A10
Solid Epoxy Resin master-batch resin containing 10%wt of a silicone free flow agent. |
Solid Epoxy Resins | Specialty Solid Epoxy Resins | 780 – 900 | – | 2,800 – 5,000 (1) | 98 – 106 | 100 | EMEAI, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 640
Chemically modified epoxy resin with low surface tension offering excellent flow and pigment / substrate wetting |
Solid Epoxy Resins | Specialty Solid Epoxy Resins | 840 – 940 | – | NA | 93 – 103 | 100 | EMEAI | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 642U
Novolac modified solid resin for functional powder coatings. In combination with other resins provides excellent corrosion and chemical resistance combined with good mechanical properties. Typical applications include pipe coatings and internal drum linings. |
Solid Epoxy Resins | Specialty Solid Epoxy Resins | 520 – 560 | – | 1,900 – 3,300 (1) | 92 – 98 | 100 | LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 642U-20
Novolac modified solid resin for functional powder coatings. In combination with other resins provides excellent corrosion and chemical resistance combined with good mechanical properties. Typical applications include pipe coatings and internal drum linings. |
Solid Epoxy Resins | Specialty Solid Epoxy Resins | 500 – 560 | – | 1,900 – 3,300 (1) | 89 – 97 | 100 | APAC, EMEAI | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 6508
Specialty resin designed for high glass transition temperature Fusion Bonded Epoxy coatings ( up to 140 °C) |
Solid Epoxy Resins | High Performance Powder Coating Resins | 380 – 420 | – | 7,000 – 9,500 (1) | 95 – 105 | 100 | APAC, EMEAI, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 6510 HT
Specialty resin designed for high glass transition temperature Fusion Bonded Epoxy coatings ( up to 160 °C) |
Solid Epoxy Resins | High Performance Powder Coating Resins | 410 – 440 | – | 7,000 – 9,500 (1) | 105 – 114 | 100 | APAC, EMEAI, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 660
Semi-solid epoxy resin for composites or high solids coatings. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 315 – 335 | – | 3,500 – 7,000 (3) | NA | 100 | EMEAI | (3) 80 wt% in Xylene |
|
D.E.R.® 661
Unmodified standard “1-type” solid epoxy resin. Excellent base for many high quality chemical-resistant coatings withstanding exposure to corrosive atmospheres. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 500 – 560 | – | 400 – 800 (1) | 75 – 85 | 100 | LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 6615
Low application temperature cure, down to approximately 110 °C, solid epoxy resin. Based on Dow patented process technology which allows combination of low melt viscosity whilst retaining sufficiently high softening point. |
Solid Epoxy Resins | High Performance Powder Coating Resins | 500 – 550 | – | < 1000 (1) | 78 – 86 | 100 | APAC, EMEAI, LAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 661E
Unmodified standard “1-type” solid epoxy resin. Excellent base for many high quality chemical-resistant coatings withstanding exposure to corrosive atmospheres. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 495 – 525 | – | 550 – 830 (1) | 78 – 84 | 100 | APAC, EMEAI | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 6625
Low molecular weight “2.5-Type” epoxy resin. Slightly different equivalent weight to melt-viscosity balance. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 610 – 650 | – | 1,500 – 2,000 (1) | 81 – 101 | 100 | EMEAI | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 662E
Standard “2-type” epoxy resin for excellent flow in standard as well as in low application temperature cure applications. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 590 – 630 | – | 1,100 – 2,100 (1) | 87 – 93 | 100 | APAC, EMEAI, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 662UH
Low molecular weight “2.5-type” epoxy resin for decorative powders coatings requiring excellent gloss and flow. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 675 – 750 | – | 1,600 – 3,000 (1) | 90 – 98 | 100 | LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 6635
Low molecular weight “3.5-Type” epoxy resin. Slightly different equivalent weight to melt-viscosity balance. |
Solid Epoxy Resins | Medium Molecular Weight Solid Epoxy Resin | 730 – 830 | – | 3,500 – 5,500 (1) | 95 – 101 | 100 | EMEAI | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 663U
Medium molecular weight “3-type” epoxy resin for both pure epoxy and epoxy/polyester hybrid powder coatings requiring good gloss, smoothness and excellent flexibility. |
Solid Epoxy Resins | Medium Molecular Weight Solid Epoxy Resin | 730 – 820 | – | 2,000 – 4,000 (1) | 92 – 102 | 100 | APAC, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 663UE
Medium molecular weight “3-type” epoxy resin for both pure epoxy and epoxy/polyester hybrid powder coatings requiring good gloss, smoothness and excellent flexibility. |
Solid Epoxy Resins | Medium Molecular Weight Solid Epoxy Resin | 740 – 800 | – | 3,100 – 5,200 (1) | 98 – 104 | 100 | APAC, EMEAI, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 664
Medium molecular weight “4-type” epoxy resin containing an esterification catalyst. Esters prepared by reacting this resin with fatty acids have very consistent viscosities and acid values. |
Solid Epoxy Resins | Medium Molecular Weight Solid Epoxy Resin | 875 – 955 | – | 4,000 – 8,000 (1) | 100 – 110 | 100 | LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 664-HA
Chemically modified medium molecular weight solid epoxy resin offering significantly improved hot/wet adhesion and cathodic disbondment. |
Solid Epoxy Resins | High Performance Powder Coating Resins | 750 – 850 | – | 5,000 – 10,000 (1) | 105 – 115 | 100 | EMEAI, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 664U
Medium molecular weight “4-type” epoxy resin for both decorative and functional coatings to provide improved viscosity characteristics and greater flexibility. |
Solid Epoxy Resins | Medium Molecular Weight Solid Epoxy Resin | 875 – 955 | – | 4,000 – 8,000 (1) | 100 – 110 | 100 | APAC, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 664UE
Medium molecular weight “4-type” epoxy resin for both decorative and functional coatings to provide improved viscosity characteristics and greater flexibility. |
Solid Epoxy Resins | Medium Molecular Weight Solid Epoxy Resin | 860 – 930 | – | 5,500 – 10,200 (1) | 104 – 110 | 100 | APAC, EMEAI, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 667-20
Higher reactivity, high molecular weight “7-type” solid epoxy resin. Suitable for metal decoration, interior and exterior can coatings, tube and drum linings, coil primers and many other industrial applications. |
Solid Epoxy Resins | High Molecular Weight Solid Epoxy Resins | 1,600 – 1,950 | – | 1,300 – 4,000 (2) | 125 – 138 | 100 | APAC, EMEAI, LAA, NAA | 1 cSt @25 °C,40 wt% in diethylene glycol monobutyl ether |
|
D.E.R.® 667E
High molecular weight “7 type” solid epoxy resin with improved solution stability. Suitable for metal decoration, interior and exterior can coatings, tube and drum linings, coil primers and many other industrial applications. |
Solid Epoxy Resins | High Molecular Weight Solid Epoxy Resins | 1,600 – 1,950 | – | 2,000 – 2,900 (2) | 126 – 137 | 100 | APAC, EMEAI, LAA, NAA | 1 @25 °C,40 wt% in diethylene glycol monobutyl ether |
|
D.E.R.® 668-20
High molecular weight “8 type” epoxy resin designed for can & coil coatings. Offers improved flexibility versus equivalent 7-type epoxy resins. |
Solid Epoxy Resins | High Molecular Weight Solid Epoxy Resins | 2,000 – 3,500 | – | 2,700 – 5,000 (2) | 135 – 146 | 100 | EMEAI, LAA, NAA | 1 @25 °C,40 wt% in diethylene glycol monobutyl ether |
|
D.E.R.® 669-20
Highest molecular weight solid epoxy resin, of the “9-type”, for can & coil coatings. Offers enhanced reactivity versus the E-version. |
Solid Epoxy Resins | High Molecular Weight Solid Epoxy Resins | 3,500 – 5,500 | – | 4,400 – 10,000 (2) | 142 – 164 | 100 | EMEAI, LAA, NAA | 1 @25 °C,40 wt% in diethylene glycol monobutyl ether |
|
D.E.R.® 669E
Highest molecular weight solid epoxy resin, of the “9-type”, for can & coil coatings. Shows improved solution storage stability. |
Solid Epoxy Resins | High Molecular Weight Solid Epoxy Resins | 2,500 – 4,000 | – | 4,500 – 10,000 (2) | 142 – 164 | 100 | APAC, EMEAI, LAA, NAA | 2 @25 °C,40 wt% in diethylene glycol monobutyl ether |
|
D.E.R.® 671
Low molecular weight “1-type” solid epoxy resin designed for room temperature curing wet paints. Industry standard for heave duty anti-corrosion paints for which many solutions exists. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 475 – 550 | – | 400 – 950 (1) | 75 – 85 | 100 | APAC, EMEAI, LAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 672U
Novolac modified, higher molecular weight solid epoxy resin for more flexible, corrosion resistant epoxy powder coating. Extra edge-coverage can be obtained by the addition of 10-50% of this resin grade to the pipe or internal drum lining formulation. |
Solid Epoxy Resins | Specialty Solid Epoxy Resins | 750 – 850 | – | 15,000 – 40,000 (1) | 110 – 120 | 100 | APAC, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 672U-20
Novolac modified, higher molecular weight solid epoxy resin for more flexible, corrosion resistant epoxy powder coating. Extra edge-coverage can be obtained by the addition of 10-50% of this resin grade to the pipe or internal drum lining formulation. |
Solid Epoxy Resins | Specialty Solid Epoxy Resins | 740 – 830 | – | 15,000 – 40,000 (1) | 110 – 120 | 100 | EMEAI | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 692
Low molecular weight “2.5-type” epoxy resin for decorative powders coatings requiring excellent gloss and flow. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 660 – 720 | – | 1,700 – 2,500 (1) | 87 – 97 | 100 | APAC, EMEAI, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 692H
Low molecular weight “2.5-type” epoxy resin containing 2 wt% of a polyacrylate flow modifier. The flow modifier is different than in D.E.R. 692HB epoxy resin. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 660 – 720 | – | 1,600 – 2,400 (1) | 89 – 97 | 100 | EMEAI, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 692HB
Low molecular weight “2.5-type” epoxy resin containing 2.5 wt% of a polyacrylate flow modifier. The flow modifier is different than in D.E.R. 692H epoxy resin. |
Solid Epoxy Resins | Low Molecular Weight Solid Epoxy Resin | 660 – 720 | – | 1,600 – 2,400 (1) | 89 97 | 100 | EMEAI | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 732P
Longer chain polyglycol diepoxide liquid resin for improved flexibility, elongation and impact resistance in coatings and adhesives. |
Epoxy Toughening / Flexibilizing Solutions | Flexible Epoxy Resins, Reactive Diluents | 310 – 330 | – | 60 – 70 | – | – | EMEAI | – |
|
D.E.R.® 736P
Shorter chain polyglycol diepoxide liquid resin for improved flexibility, elongation and impact resistance in coatings and adhesives. |
Epoxy Toughening / Flexibilizing Solutions, Reactive Diluents | Low Viscosity Epoxy Resins | 175 – 205 | – | 30 – 60 | – | – | EMEAI | – |
|
D.E.R.® 750
Flexibilised epoxy resin suitable for civil engineering compounds (crack bridging), adhesives or for improvement of the toughness of fiber reinforced composites. |
Epoxy Toughening / Flexibilizing Solutions | Flexible Epoxy Resins | 176 – 186 | – | 2,500 – 4,500 | – | – | NAA | – |
|
D.E.R.® 8230W5
Master batch resin for powder coatings. The siloxane flow modifier provides maximum transparency in clear powder coatings. Also the flow modifier provides good slip and mar resistance. |
Solid Epoxy Resins | Specialty Solid Epoxy Resins | 770-860 | – | 800 – 3,500 (1) | 82 – 92 | 100 | APAC, NAA | (1) Melt viscosity at 150 ᵒC |
|
D.E.R.® 852
Mid Viscosity Epoxy Functional Reactive Toughening Agent. |
Epoxy Toughening / Flexibilizing Solutions | Toughened Epoxy Resins | 300 – 340 | – | 7,000 – 17,000 | – | 55 | EMEAI | – |
|
D.E.R.® 858
Mid molecular weight oxazolidone modified solid epoxy resin |
Epoxy Toughening / Flexibilizing Solutions | Toughened Epoxy Resins | 380 – 420 | – | 2,800 – 4,200 (1) | 95 – 105 | – | APAC, EMEAI | 1 @ 150 °C |
|
D.E.R.® 913
Liquid epoxy resin emulsion with improved reactivity, designed for 2 component coating systems. |
Waterborne Systems | Emulsions and Dispersions | 167 – 193 | – | 100 – 400 | – | 67 | EMEAI, LAA | – |
|
D.E.R.® 915
Dispersion of a 1-type solid epoxy resin, similar to D.E.R.® 671 epoxy resin, in water with very low average particle size and narrow distribution. Absolute VOC-free for medium-high anti-corrosion paints. Also suitable for fast drying floor coatings. |
Waterborne Systems | Emulsions and Dispersions | 475 – 500 | – | 3,000 – 9,000 | – | 47 | APAC, EMEAI, LAA, NAA | – |
|
D.E.R.® 916
Emulsion of an epoxy novolac resins, similar to D.E.N.® 438 epoxy novolac, in water. For high chemical resistance and/or high temperature resistance coating applications. |
Waterborne Systems | Emulsions and Dispersions | 184 – 204 | – | 5,000 – 1,0000 | – | 58 | APAC, EMEAI, LAA, NAA | – |
|
D.E.R.® 917
Emulsion of a standard bisphenol-A liquid epoxy resin, similar to D.E.R. 331® epoxy resin, in water. 100% VOC free. Designed for civil engineering applications requiring improved crosslink density, solvent resistance and hardness. Also suitable as co-reactant in other aqueous systems. |
Waterborne Systems | Emulsions and Dispersions | 193 – 204 | – | 3,000 – 9,000 | – | 64 | APAC, EMEAI, LAA, NAA | – |
|
DLVE® 18
Low viscosity liquid epoxy resin modified with a Cycloaliphatic polyglycidyl ether for high solids coating formulations with ultra low volatile organic compound (VOC) emissions and ease of application. Excellent corrosion protection and chemical resistance. Can be cured with multiple types of curing agents (hardeners) |
DLVE® & DLVNE®, Liquid Epoxy Resins | Low Viscosity Epoxy Resins | 160 – 175 | – | 400 – 1,000 | – | 100 | APAC, EMEAI, LAA, NAA | – |
|
DLVE® 52
Ultra Low viscosity epoxy resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) for high solids coating formulations with low volatile organic compound (VOC) emissions, excellent application, corrosion and chemical resistance. This resin is more hydrophobic and can provide better surface wetting. Can be cured with multiple types of curing agents (hardeners) |
DLVE® & DLVNE®, Liquid Epoxy Resins | Low Viscosity Epoxy Resins | 165 – 180 | – | 350 – 550 | – | 100 | APAC, EMEAI, LAA, NAA | – |
|
DLVNE 59
Low viscosity Novolac resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) for high solids coating formulations with low volatile organic compound (VOC) emissions. Balance of properties similar to solvent borne Novolac. |
DLVE® & DLVNE® | Low Viscosity Epoxy Novolac Resins | 160 – 175 | – | 2,000 – 4,000 | – | 100 | APAC, EMEAI, LAA, NAA | – |
|
DLVNE® 59
Low viscosity Novolac resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) for high solids coating formulations with low volatile organic compound (VOC) emissions. Balance of properties similar to solvent borne Novolac. |
Epoxy Novolac Resins | Low Viscosity Epoxy Novolac Resins | 160 – 175 | – | 2,000 – 4,000 | – | 100 | APAC, EMEAI, LAA, NAA | – |
|
DLVNE 61
Medium low viscosity Novolac resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) that facilitate high solids coating formulations with low volatile organic compound (VOC) emissions, improved application, strong chemical and thermal resistance. |
DLVE® & DLVNE® | Low Viscosity Epoxy Novolac Resins | 155 – 170 | – | 4,500 – 6,500 | – | 100 | APAC, EMEAI, LAA, NAA | – |
|
DLVNE® 61
Medium low viscosity Novolac resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) that facilitate high solids coating formulations with low volatile organic compound (VOC) emissions, improved application, strong chemical and thermal resistance. |
Epoxy Novolac Resins | Low Viscosity Epoxy Novolac Resins | 155 – 170 | – | 4,500 – 6,500 | – | 100 | EMEAI, LAA | – |
|
FORTEGRA® 104
Specialty 4-type solid epoxy resin with improved toughness and impact resistance designed for fusion bonded epoxy abrasion resistant overcoats. |
Epoxy Toughening / Flexibilizing Solutions | Toughened Epoxy Resins | 960 – 1,060 | – | 4,500 – 9,500 (1) | NA | – | EMEAI, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
FORTEGRA® 104
Specialty 4-type solid epoxy resin with improved toughness and impact resistance designed for fusion bonded epoxy abrasion resistant overcoats. |
Solid Epoxy Resins | Toughened Epoxy Resins | 960 – 1,060 | – | 4,500 – 9,500 (1) | NA | 100 | EMEAI, LAA, NAA | (1) Melt viscosity at 150 ᵒC |
|
FORTEGRA® 202
Low viscosity toughener based on innovative technology. Imparts adhesion, impact resistance and anticorrosion resistance via nanometer size phase separation in curing matrix. |
Epoxy Toughening / Flexibilizing Solutions | Toughened Epoxy Resins | N/A | – | 4,500 – 8,000 | – | – | APAC, NAA | – |
|
FORTEGRA® 304
Specialty solid resin designed to improve flexibility and impact resistance of fusion bonded epoxy coatings |
Epoxy Toughening / Flexibilizing Solutions | Toughened Epoxy Resins | 920 – 1,090 | – | 8,000 – 23,000 (1) | 105 – 115 | – | APAC, EMEAI, LAA | 1 @ 150 °C |
|
FORTEGRA® 304
Specialty solid resin designed to improve flexibility and impact resistance of fusion bonded epoxy coatings |
Solid Epoxy Resins | Toughened Epoxy Resins | 920 – 1,090 | – | 8,000 – 23,000 (1) | 105 – 115 | 100 | APAC, EMEAI, LAA | (1) Melt viscosity at 150 ᵒC |
|
FORTEGRA® 310
Specialty resin designed to improve flexibility and impact resistance of fusion bonded epoxy coatings with high glass transition temperature ( up to 160 °C) |
Epoxy Toughening / Flexibilizing Solutions | Toughened Epoxy Resins | 400 – 450 | – | 5,000 – 15,000 (1) | 105 – 117 | – | APAC, EMEAI, LAA | – |
|
FORTEGRA® 310
Specialty resin designed to improve flexibility and impact resistance of fusion bonded epoxy coatings with high glass transition temperature ( up to 160 °C) |
Solid Epoxy Resins | Toughened Epoxy Resins | 400 – 450 | – | 5,000 – 15,000 (1) | 105 – 117 | 100 | APAC, EMEAI, LAA | (1) Melt viscosity at 150 ᵒC |
|
FORTEGRA® 352
A stable dispersion of preformed novel Core Shell Rubber (CSR) particles in a bisphenol A liquid epoxy resin containing 33wt% of the CSR. |
Epoxy Toughening / Flexibilizing Solutions | Toughened Epoxy Resins | 248 – 268 | – | 17,000 – 23,000 (2) | – | – | APAC, LAA, NAA | (2) @ 50 °C |
|
XU 19651
Blend of D.E.N. 438 and difunctional reactive diluent for easier handling for flooring and grouts. |
Epoxy Novolac Resins | Epoxy Novolac Resins | 145 – 158 | – | 300 – 500 | – | 100 | LAA, NAA | – |
|
XZ 97103.00
Low molecular weight high Tg epoxy resin modified with oxazolidone to improve tougness. To be used as an adhesion promoter as well. |
Epoxy Toughening / Flexibilizing Solutions | Toughened Epoxy Resins | 280 – 305 | – | 500 – 2,500 | – | 74 – 76 | APAC | – |