Products for Composites used in Energy (Resins & Systems)

View Products
Product Name & Description Category

Type

EEW Based on solids (g/eq)

AHEW Based on solids (g/eg)

Viscosity @25°C (mPa.s)

Softening Point

Solids Content (wt%)

Pot Life Min.

Regional Availability

APAC - Asia, Pacific
EMEAI - Europe, Middle East, Africa, India
LAA - Latin America Area
NAA - North America Area
Footnote

D.E.H.™ 800

Polyamine adduct hardener DISSOLVED in water (storage/shear stable). Alkali-resistant so useful for ECC. Visible end of pot-life. In combination with solid epoxy emulsion suitable for corrosion protection on steel. Can be used on fresh concrete (immediately after being laid).

Waterborne Systems Waterborne Epoxy Curing Agents 150 5,000 – 1,0000 50 APAC, EMEAI, LAA, NAA
D.E.H.™ 804

Aqueous polyamine adduct solution with emulsification capability. Offers visible end of pot life, fast drying, low odor. Suitable for thick layer self leveling applications.

Waterborne Systems Waterborne Epoxy Curing Agents 123 5,000 – 11,000 70 EMEAI, NAA
D.E.H.™ 805

Standard for Coating on Concrete. Not compatible with Zink Phosphates. Calcium phosphates could be used but more expensive. Visible end of pot-life. D.E.H. 805 allows to develop roller coat formulations with a matte, satin or high gloss finish.

Waterborne Systems Waterborne Epoxy Curing Agents 220 10,000 – 19,000 65 APAC, EMEAI, LAA, NAA
D.E.H.™ 806

Polyamine-adduct designed for best corrosion protection. Can handle anti-corrosion pigments. Avoid dispersion shear of >40°C. No visible end of pot-life.

Waterborne Systems Waterborne Epoxy Curing Agents 160 9,500 – 15,500 80 APAC, EMEAI, LAA
D.E.H.™ 810

Designed for best corrosion protection. Not compatible with anti-corrosion pigments (zinc-phosphates). Best for clear coatings with solid epoxy dispersions. Show excellent adhesion to diamonds (Closest we have to Waterpoxy 751).

Waterborne Systems Waterborne Epoxy Curing Agents 150 2,000 – 4,000 50 APAC, EMEAI, LAA, NAA
D.E.H.™ 813

Designed for faster curing corrosion protection, i.e. faster version of 7006. Can handle zinc phosphate (anti-corrosion pigments). NO visible end of pot life with solid epoxy resin dispersions. Should not be used in too thick layer > 300 mu otherwise “mud-cracking” can occur. Can be dust-free in 30 minutes (when formulated)

Waterborne Systems Waterborne Epoxy Curing Agents 140 5,000 – 1,0000 70 APAC, EMEAI, LAA
D.E.H.™ 820

Waterborne amine-adduct curing agent without free amine. Suitable for use in applications requiring German potable water contact certification.

Waterborne Systems Waterborne Epoxy Curing Agents 205 16,000 – 18,000 70 EMEAI
D.E.N.™ 424

Approximately 2.4 functional low viscosity liquid epoxy novolac resin. D.E.N. 424 fills the gap between the standard Bisphenol F based liquid epoxy resin and multifunctional, low viscosity epoxy novolac resin D.E.N 425. Compared to standard Bisphenol A and Bisphenol F based liquid epoxy resins, D.E.N. 424 produces an improved crosslinked system, which enables better thermal and chemical resistance with a low viscosity that is necessary for easy processing and application.

Epoxy Novolac Resins Epoxy Novolac Resins 165 – 175 5,700 – 6,800 LAA, NAA
D.E.N.™ 425

Approximately 2.5 functional liquid epoxy novolac resin bridging between standard liquid epoxy resin and semi-solid epoxy novolac resins. When used in combination with a fast curing agent no post-cure is required and binder systems are obtained with excellent mechanical and especially solvent resistance properties.

Epoxy Novolac Resins Epoxy Novolac Resins 169 – 175 9,500 – 12,500 100 APAC, EMEAI, LAA, NAA
D.E.N.™ 428

Multi-functional (±2.8) epoxy novolac resin of lower viscosity compared to the higher viscosity epoxy novolac epoxy resin D.E.N. 431. In addition to improved processing of this medium viscosity novolac resin, D.E.N. 428 is distinguished by particularly good thermal resistance, chemical resistance, and mechanical properties. With these characteristic properties, D.E.N. 428 is suitable for applications such as protective coatings or linings for storage tanks, pipes, and pumps.

Epoxy Novolac Resins Epoxy Novolac Resins 168 – 178 35,000 – 45,000 LAA, NAA
D.E.N.™ 431

Multi-functional (±2.8) epoxy novolac resin of lower molecular weight for application where solvents cannot be tolerated and application viscosity (temperature) needs to remain relatively low. Used in adhesives, electrical and structural laminates and castings for elevated temperature service and excellent chemical resistance.

Epoxy Novolac Resins Epoxy Novolac Resins 172 – 179 1,100 – 1,700 (1) 100 APAC, EMEAI, LAA, NAA 1 at 51.7°C
D.E.N.™ 431 EK98

Solution of D.E.N. 431 in methyl-ethyl ketone.

Epoxy Novolac Resins Epoxy Novolac Solutions 172 – 179 5,000 – 25,000 98 NAA
D.E.N.™ 438™

Highly functional (±3.6) epoxy novolac resin offering best mechanical, temperature and chemical resistance performance with acceptable viscosity. Recognized as a standard for high-temperature applications.

Epoxy Novolac Resins Epoxy Novolac Resins 176 – 181 31,000 – 40,000 (1) 100 APAC, EMEAI, LAA, NAA 1 at 51.7°C
D.E.N.™ 438-A85

Solution of D.E.N. 438 in acetone mainly for laminating or Prepreg applications.

Epoxy Novolac Resins Epoxy Novolac Solutions 176 – 181 500 – 1,200 84 – 86 APAC, NAA
D.E.N.™ 438-EK85

Solution of D.E.N. 438 in methyl-ethyl ketone mainly for laminating or Prepreg applications.

Epoxy Novolac Resins Epoxy Novolac Solutions 176 – 181 600 – 1,600 84 – 86 APAC, EMEAI, NAA
D.E.N.™ 438-MAK80

Solution of D.E.N. 438 in methyl n-amyl ketone mainly for laminating or Prepreg applications.

Epoxy Novolac Resins Epoxy Novolac Solutions 176 – 181 600 – 1,200 79 – 81 NAA
D.E.N.™ 438-MK75

Solution of D.E.N. 438 in methyl iso-butyl ketone mainly for laminating or Prepreg applications.

Epoxy Novolac Resins Epoxy Novolac Solutions 176 – 181 200 – 600 74 – 76 NAA
D.E.N.™ 438-X80

Solution of D.E.N. 438 in Xylene. Main use in wet-paint systems with high temperature or chemical resistance requirements.

Epoxy Novolac Resins Epoxy Novolac Solutions 176 – 181 1,200 – 2,000 79 – 81 APAC, EMEAI, NAA
D.E.N.™ 438L

Low(er) viscosity version of D.E.N. 438 epoxy novolac resin to allow higher solids and/or lower viscosity formulations.

Epoxy Novolac Resins Epoxy Novolac Resins 176 – 181 27,500 – 32,500 (1) 100 NAA 1 at 51.7°C
D.E.N.™ 439

Highly functional (±3.8) epoxy novolac resin with improved reactivity. The higher viscosity offers a means of obtaining good drape and limited tack in Prepreg formulations.

Epoxy Novolac Resins Epoxy Novolac Resins 191 – 210 15,000 – 35,000 (2) 100 APAC, EMEAI, NAA 2 at 71°C
D.E.N.™ 439-EK85

Solution of D.E.N. 439 in methyl-ethyl ketone mainly for laminating or Prepreg applications.

Epoxy Novolac Resins Epoxy Novolac Solutions 191 – 210 4,000 – 10,000 84 – 86 APAC, EMEAI, NAA
D.E.N.™ 439-H

Highly functional epoxy novolac resin with lower processing variability.

Epoxy Novolac Resins Epoxy Novolac Resins 191 – 210 23,000 – 29,000 (2) 100 NAA 2 at 71°C
D.E.N.™ 440

Extremely high functional (± 4.4) epoxy novolac resin. Offers highest performance in this product group with regards to mechanical, temperature and chemical resistance properties.

Epoxy Novolac Resins Epoxy Novolac Resins 187 – 192 50,000 – 90,000 (2) 100 EMEAI, NAA 2 at 71°C
D.E.R.™ 301

Modified liquid epoxy resin; compared with standard bisphenol A based liquid epoxy resin, similar viscosity, improved flexibility, longer pot life and anticorrosion performance; suitable for high solids (80% volume solid above) formulation.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 245 – 265 10,000 – 14,000 100 APAC
D.E.R.™ 3113

Extreme low viscosity resin for .crack injection and sealing

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 178 – 197 250 – 350 100 EMEAI
D.E.R.™ 317

High viscosity, fast reacting (20% faster than D.E.R. 331) liquid epoxy resin designed for adhesive applications requiring quick gelling with amine curing agents.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 192 – 203 16,000 – 25,000 100 NAA
D.E.R.™ 321

Very low viscosity resin allowing large amounts of fillers. Cure rate similar to undiluted resins. Improved acid resistance can be observed. For floorings, grouting, concrete reinforcement, structural adhesives, crack injection and castings.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 180 – 188 500 – 700 100 EMEAI, LAA, NAA
D.E.R.™ 3212

Similar to D.E.R. 321 epoxy resin but of higher viscosity maintaining more mechanical strength.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 179 – 193 750 – 1,400 100 LAA, NAA
D.E.R.™ 322

Low diluent content resin combining significant viscosity reduction whilst maintaining mechanical strength properties.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 183 – 193 5,500 – 8,500 100 NAA
D.E.R.™ 3221

Liquid epoxy resin especially suitable for use in water borne epoxy binder systems.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 187 – 208 700 – 1,000 100 EMEAI
D.E.R.™ 323

Low viscosity liquid epoxy resin with reduced surface tension. Offers excellent wetting and flow. The low diluent content is the cause of the improved mechanical properties over D.E.R. 324 epoxy resin.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 190 – 204 1,000 – 1,200 100 NAA
D.E.R.™ 324

Offers low viscosity and low surface tension to wet the surface better, giving better adhesion and slightly lower viscosity at any given filler loading. The diluent increases pot life, flexibility (impact resistance) and acid resistance.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 195 – 204 600 – 800 100 APAC, EMEAI, LAA, NAA
D.E.R.™ 325

Low viscosity liquid epoxy resin with reduced surface tension. Offers excellent wetting and flow. The low diluent content is the cause of the improved mechanical properties over D.E.R. 323 and D.E.R. 324 epoxy resin.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 185 – 206 850 – 2,800 100 NAA
D.E.R.™ 326

Low viscosity liquid epoxy resin with minimal crystallization tendency. Offers low surface tension, excellent wetting and flow.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 204 – 210 600 – 900 100 NAA
D.E.R.™ 3271

Very low viscosity epoxy resin designed for mineral castings in combination with e.g. D.E.H. 2112 epoxy curing agent.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 156 – 170 250 – 450 100 EMEAI
D.E.R.™ 3274

Bi-functional reactive diluent containing resin offering reduced viscosity whilst only affecting the mechanical and thermal properties moderately.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 160 – 180 1,300 – 1,500 100 EMEAI, LAA, NAA
D.E.R.™ 3282

Reactive diluent containing epoxy resin offering low viscosity, good mechanical properties as well as solvent resistance.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 173 – 183 900 – 1,100 100 EMEAI
D.E.R.™ 3284

Medium viscosity liquid epoxy resin with di-functional reactive diluent. Especially suited for lamination purposes where it shows excellent wetting of the fabric and gives outstanding mechanical properties.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 173 – 185 2,400 – 2,900 100 EMEAI
D.E.R.™ 329

Low viscosity epoxy resin with very good thermal properties, and excellent fatigue behavior. Allows fast low temperature cure, and improved solvent resistance. For use in coatings for tank-linings and solvent-free/high solids epoxy binders.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 145 – 155 900 – 1,300 100 EMEAI, LAA, NAA
D.E.R.™ 330

D.E.R. 330 epoxy resin is a low viscosity bisphenol A epoxy resin commonly used in composite and casting applications. D.E.R. 330 epoxy resin frequently crystallizes at room temperature; heating to 50-55°C restores the resin to liquid state. Long-term warm storage may result in slight discoloration but does not affect the resin performance.

Liquid Epoxy Resins Bisphenol A Liquid Epoxy Resins 176 – 185 7,000 – 10,000 100 EMEAI, NAA
D.E.R.™ 330-EL

Lower viscosity bisphenol-A epoxy resin with very low hydrolysable chloride content (<100 ppm). Specifically suitable for electrical, electronic and encapsulation applications.

Liquid Epoxy Resins Bisphenol A Liquid Epoxy Resins 176 – 185 7,000 – 10,000 100 EMEAI
D.E.R.™ 331™

Industry standard bisphenol-A based liquid epoxy resin. Offers excellent mechanical, thermal and chemical resistance properties in multiple applications. Shows improved reactivity and wetting properties versus competitive alternatives.

Liquid Epoxy Resins Bisphenol A Liquid Epoxy Resins 182 – 192 11,000 – 14,000 100 APAC, EMEAI, LAA, NAA
D.E.R.™ 331-EL

Standard bisphenol-A epoxy resin with very low hydrolysable chloride content (<150 ppm). Specifically suitable for electrical, electronic and encapsulation applications.

Liquid Epoxy Resins Bisphenol A Liquid Epoxy Resins 182 – 192 11,000 – 14,000 100 APAC, EMEAI
D.E.R.™ 331LS

Low Sodium content reaction product of epichlorohydrin and Bisphenol A

Liquid Epoxy Resins Bisphenol A Liquid Epoxy Resins 186 – 190 11,000 – 13,500 100 NAA
D.E.R.™ 332

High purity diglycidylether ether of bisphenol A. Its high purity and low oligomer content assures uniform performance, exceptionally low viscosity and improved elevated temperature properties over standard epoxy resins. This resin grade is mainly used in electrical encapsulation applications.

Liquid Epoxy Resins Bisphenol A Liquid Epoxy Resins 171 – 175 4,000 – 6,000 100 APAC, EMEAI, NAA
D.E.R.™ 336

Standard liquid bisphenol-A epoxy resin of intermediate viscosity and equivalent weight with narrow specification limits.

Liquid Epoxy Resins Bisphenol A Liquid Epoxy Resins 181 – 185 9,400 – 11,000 100 EMEAI
D.E.R.™ 336-EL

Intermediate viscosity epoxy resin with very low hydrolysable chloride content (<150 ppm). Specifically suitable for electrical, electronic and encapsulation applications.

Liquid Epoxy Resins Bisphenol A Liquid Epoxy Resins 181 – 185 9,400 – 11,000 100 EMEAI
D.E.R.™ 337

Intermediate epoxy equivalent weight semi-solid epoxy resin, mainly used in adhesives and protective coatings, or as a modifier for other epoxy resins to improve impact strength, extensibility and adhesion.

Liquid Epoxy Resins Bisphenol A Liquid Epoxy Resins 230 – 250 400 – 800 (1) 100 EMEAI (1) 70 wt% in diethylene glycol monobutyl ether
D.E.R.™ 337-DA97

Solution of D.E.R. 337 in diacetone alcohol.

Liquid Epoxy Resins Epoxy Resin Solutions 230 – 278 NA 96 – 98 NAA
D.E.R.™ 337-X80

Solution of D.E.R. 337 in xylene. The excellent resistance and physical properties for epoxy coal tar combinations and higher solids content marine coatings.

Liquid Epoxy Resins Epoxy Resin Solutions 230 – 260 500 – 1,200 79 – 81 EMEAI, NAA
D.E.R.™ 337-X90

Solution of D.E.R. 337 in xylene. Higher solids content than D.E.R. 337-X80 epoxy resin solution.

Liquid Epoxy Resins Epoxy Resin Solutions 230 – 250 5,000 – 15,000 89 – 91 NAA
D.E.R.™ 338-X90

Solution of a semi-solid epoxy resin in xylene.

Liquid Epoxy Resins Epoxy Resin Solutions 230 – 280 5,000 – 50,000 89 – 91 NAA
D.E.R.™ 3401

Low viscosity rapidly reacting Bisphenol A/F epoxy resin designed for fast-curing coatings, adhesives, and mortars. It can be used as the sole epoxy or in combination with other epoxy resins. Rapid cure, return to service, Low emissions or substance of concern content, Low viscosity, Good chemical resistance

Liquid Epoxy Resins Modified Bisphenol A/F Liquid Epoxy Resins 175 – 215 1,500 – 3,500 100 NAA
D.E.R.™ 3411

Accelerated, crystallization stable liquid epoxy resin.

Liquid Epoxy Resins Accelerated Epoxy Resins 185 – 205 4,500 – 5,500 100 EMEAI
D.E.R.™ 3412

Accelerated modified bisphenol-A/F epoxy resin of low viscosity.

Liquid Epoxy Resins Accelerated Epoxy Resins 187 – 207 850 – 1,150 100 EMEAI
D.E.R.™ 3414

Master-batch accelerated epoxy resin with a catalyst active at room temperature. Allows shorter gel and drying times in room temperature cure and fast cycling times in composites applications.

Liquid Epoxy Resins Accelerated Epoxy Resins 190 – 210 2500 – 4500 100 APAC, EMEAI
D.E.R.™ 3415

Master-batch accelerated epoxy resin with a catalyst active at temperatures of 60 °C and above. Used in composite, heat cure, applications for fast cycling times.

Liquid Epoxy Resins Accelerated Epoxy Resins 190 – 210 2500 – 4500 100 EMEAI
D.E.R.™ 351

D.E.R. 351 liquid epoxy resin is a low viscosity epoxy resin combining the performance properties of standard bisphenol A epoxy resin with the low viscosity of bisphenol F epoxy resin. The resin blend shows a low tendency to crystallization. Applications include solvent-free coatings, tank- and pipe-linings, concrete reinforcements and also floorings, adhesives, electrical insulation and filament winding.

Liquid Epoxy Resins Bisphenol A/F Liquid Epoxy Resins 169 – 181 4,500 – 6,500 100 APAC, EMEAI
D.E.R.™ 352

Higher viscosity and more economic bisphenol-A/F liquid epoxy resin. Recommended base for many modified bisphenol-A/F liquid epoxy resins.

Liquid Epoxy Resins Bisphenol A/F Liquid Epoxy Resins 172 – 181 5,700 – 7,700 100 EMEAI, NAA
D.E.R.™ 353

Low viscosity epoxy resin with very low crystallization tendency. Offers low surface tension to wet the surface better, giving better adhesion. The diluent increases pot life, flexibility (impact resistance) and acid resistance.

Liquid Epoxy Resins Modified Bisphenol A/F Liquid Epoxy Resins 190 – 200 800 – 1,000 100 APAC, LAA, NAA
D.E.R.™ 3531

Low crystallization resin with low vapor pressure and hydrophobic in nature. Offers low viscosity and good wetting properties it is suitable for casting resin coatings and adhesives

Liquid Epoxy Resins Modified Bisphenol A/F Liquid Epoxy Resins 183 – 199 750 – 1,150 100 EMEAI
D.E.R.™ 3532

Low crystallization resin with low vapor pressure and hydrophobic in nature. Offers very low viscosity and good wetting properties. Similar to D.E.R. 3531 in nature.

Liquid Epoxy Resins Modified Bisphenol A/F Liquid Epoxy Resins 181 – 200 500 – 900 100 EMEAI
D.E.R.™ 3533

Low crystallization resin with low vapor pressure and hydrophobic in nature. Offers extremely low viscosity and good wetting properties. Similar to D.E.R. 3531/3532 in nature.

Liquid Epoxy Resins Modified Bisphenol A/F Liquid Epoxy Resins 187 – 200 450 – 550 100 EMEAI
D.E.R.™ 354

Unmodified bisphenol F-based epoxy resin of low viscosity. Improves crystallization resistance of other epoxy resins and gives improvement in solvent resistance. Frequently used in solvent-free coatings, floor coverings, adhesives or composite applications.

Liquid Epoxy Resins Bisphenol F Epoxy Resins 167 – 174 3,400 – 4,200 100 APAC, LAA, NAA
D.E.R.™ 3551

Low crystallization tendency modified bisphenol-A/F liquid epoxy resin. Offers excellent wetting and is recommended for floorings, mortars, grouts and adhesives.

Liquid Epoxy Resins Modified Bisphenol A/F Liquid Epoxy Resins 184 – 193 700 – 1100 100 EMEAI
D.E.R.™ 3552

Very low viscosity epoxy modified epoxy resin with fast cure and good mechanical properties. For highly fillers systems, crack injection systems or low viscous primers.

Liquid Epoxy Resins Modified Bisphenol A/F Liquid Epoxy Resins 167 – 178 400 – 600 100 EMEAI
D.E.R.™ 356

The product performance is very similar to that obtained with D.E.R. 352 Resin except that this resin will provide a more rapid cure (higher reactivity).

Liquid Epoxy Resins Bisphenol A/F Liquid Epoxy Resins 176 – 183 6,500 – 8,000 100 EMEAI
D.E.R.™ 3572

Liquid epoxy resin, modified with a di-funtional reactive diluent. Offers improved reactivity, better mechanical properties as well as solvent resistance versus mono functional aliphatic diluents.

Liquid Epoxy Resins Modified Bisphenol A/F Liquid Epoxy Resins 164 – 176 600 – 900 100 EMEAI
D.E.R.™ 3581

Liquid epoxy resin, modified with a lower vapor pressure di-functional reactive diluent. Offers improved reactivity, better mechanical properties as well as solvent resistance versus mono functional aliphatic diluents.

Liquid Epoxy Resins Modified Bisphenol A/F Liquid Epoxy Resins 169 – 180 900 – 1,400 100 EMEAI
D.E.R.™ 362

Chemically modified liquid epoxy resin without diluent. Offers excellent flow and high gloss coatings / floorings. This resin is used in building application above and below ground, on road and bridge construction, as well as in underwater applications.

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 185 – 205 4,500 – 6,500 100 NAA
D.E.R.™ 3680-X90(K)

Chemically modified low molecular weight epoxy resin in xylene. Offers lower viscosity allowing higher solids contents at similar corrosion protection properties. Improves lower temperature curing.

Liquid Epoxy Resins Epoxy Resin Solutions 230 – 270 1,200 – 3,200 89 – 91 APAC, EMEAI, LAA, NAA
D.E.R.™ 383

Lower viscosity bisphenol-A epoxy resin allowing the use of less diluents or more fillers in the formulation. Offers longer pot-life versus the standard resin and slightly improved resistance properties when used in heat curing (composite) applications.

Liquid Epoxy Resins Bisphenol A Liquid Epoxy Resins 176 – 183 9,000 – 10,500 100 APAC, LAA, NAA
D.E.R.™ 383-X20

Liquid reaction product of epichlorohydrin and Bisphenol A in xylene

Liquid Epoxy Resins Epoxy Resin Solutions 176 – 183 NA 19 – 21 NAA
D.E.R.™ 3911

Flexible hybrid epoxy resin with elongation around 200% in combination with D.E.H.™ 4723. Recommended for elastic intermediate layers.

Epoxy Toughening / Flexibilizing Solutions Flexible Epoxy Resins 374 – 416 6,500 – 9,500 EMEAI
D.E.R.™ 3912

D.E.R. 3912 is an aliphatic liquid epoxy resin flexibiliser for high solids or solvent-free coatings.

Epoxy Toughening / Flexibilizing Solutions Flexible Epoxy Resins 550 – 650 21,000 – 29,000 APAC, EMEAI
D.E.R.™ 3913

Flexible epoxy resin that offers high elongations at break at room temperature as well as at -20°C. Can be used with standard epoxy amine adduct curing agents for flooring formulations in (freezing-) cold areas.

Epoxy Toughening / Flexibilizing Solutions Flexible Epoxy Resins 345 – 365 7,500 – 9,500 APAC, EMEAI, LAA, NAA
D.E.R.™ 530-A80

Standard brominated epoxy resin in acetone with about 20.5 % bromine on solids.

Flame Retardant Systems Brominated Epoxy Resin Solution 425 – 440 1,500 – 2,500 79 – 81 EMEAI, NAA
D.E.R.™ 537 PMK 70

Standard brominated epoxy resin in Dowanol PM and MEK with about 20 % bromine on solids.

Flame Retardant Systems Brominated Epoxy Resin Solution 440 – 500 100 – 1,000 69 – 71 EMEAI, NAA
D.E.R.™ 538-A80

Brominated epoxy resin in acetone with about 20% bromine on solids. Offers less flow during lamination versus D.E.R. 530-A80 epoxy resin.

Flame Retardant Systems Brominated Epoxy Resin Solution 465 – 495 800 – 1,800 79 – 81 NAA
D.E.R.™ 539-A80

Standard brominated epoxy resin in acetone having UV blocking properties.

Flame Retardant Systems Brominated Epoxy Resin Solution 430 – 470 1,000 – 1600 79 – 81 NAA
D.E.R.™ 539-EK80

Brominated epoxy resin in methyl ethyl ketone with about 20% bromine on solids. Offers enhanced UV-blocking and fluorescence.

Flame Retardant Systems Brominated Epoxy Resin Solution 430 – 470 1,500 – 2,000 79 – 81 EMEAI
D.E.R.™ 542

Solid epoxy resin with approximately 48% bromine for flame retardancy

Flame Retardant Systems Brominated Epoxy Resins 305 – 355 NA 52 – 62 100 APAC, EMEAI, LAA, NAA
D.E.R.™ 560

Higher molecular weight solid epoxy resin with approximately 48% bromine for flame retardancy. Gives improved flexibility

Flame Retardant Systems Brominated Epoxy Resins 440 – 470 140 – 215 (1) 78 – 85 100 APAC, EMEAI, NAA (1) @ 150 ᵒC
D.E.R.™ 592-A80

Brominated epoxy resin in acetone with about 17% bromine on solids. Offers best dimensional stability and better chemical resistance that standard resins.

Flame Retardant Systems Brominated Epoxy Resin Solution 350 – 370 1,000 – 2,400 79 – 81 EMEAI, NAA
D.E.R.™ 732P

Longer chain polyglycol diepoxide liquid resin for improved flexibility, elongation and impact resistance in coatings and adhesives.

Epoxy Toughening / Flexibilizing Solutions Flexible Epoxy Resins 310 – 330 60 – 70 EMEAI
D.E.R.™ 734

1,6-hexanediol diglycidylether

Liquid Epoxy Resins, Reactive Diluents 145 – 160 10 – 30 100 EMEAI
D.E.R.™ 736P

Shorter chain polyglycol diepoxide liquid resin for improved flexibility, elongation and impact resistance in coatings and adhesives.

Epoxy Toughening / Flexibilizing Solutions Low Viscosity Epoxy Resins 175 – 205 30 – 60 EMEAI
D.E.R.™ 742

Containing on average three epoxy groups per molecule. Its higher functionality above D.E.R. 741 epoxy resin allows even better properties in most epoxy, and especially composite, applications.

Liquid Epoxy Resins 110 – 130 200 – 280 100 EMEAI
D.E.R.™ 750

Flexibilised epoxy resin suitable for civil engineering compounds (crack bridging), adhesives or for improvement of the toughness of fiber reinforced composites.

Epoxy Toughening / Flexibilizing Solutions Flexible Epoxy Resins 176 – 186 2,500 – 4,500 NAA
D.E.R.™ 791

Toughened epoxy resin with good cold elasticity and good curing rate.

Epoxy Toughening / Flexibilizing Solutions Flexible Epoxy Resins 255 – 275 28,000 – 34,000 APAC
D.E.R.™ 852

Mid Viscosity Epoxy Functional Reactive Toughening Agent.

Epoxy Toughening / Flexibilizing Solutions Toughened Epoxy Resins 300 – 340 7,000 – 17,000 55 EMEAI
D.E.R.™ 858

Mid molecular weight oxazolidone modified solid epoxy resin

Epoxy Toughening / Flexibilizing Solutions Toughened Epoxy Resins 380 – 420 2,800 – 4,200 (1) 95 – 105 APAC 1 @ 150 °C
D.E.R.™ 900

Liquid epoxy emulsion designed for use in waterborne 2-pack coating systems. Is also used as cross-linking agent for other aqueous (acrylic-) systems

Waterborne Systems Emulsions and Dispersions 193 – 204 NA 64 APAC
D.E.R.™ 913

Liquid epoxy resin emulsion with improved reactivity, designed for 2 component coating systems.

Waterborne Systems Emulsions and Dispersions 167 – 193 100 – 400 67 EMEAI, LAA
D.E.R.™ 915

Dispersion of a 1-type solid epoxy resin, similar to D.E.R. 671 epoxy resin, in water with very low average particle size and narrow distribution. Absolute VOC-free for medium-high anti-corrosion paints. Also suitable for fast drying floor coatings.

Waterborne Systems Emulsions and Dispersions 475 – 500 3,000 – 9,000 47 APAC, EMEAI, LAA, NAA
D.E.R.™ 916

Emulsion of an epoxy novolac resins, similar to D.E.N.™ 438™ epoxy novolac, in water. For high chemical resistance and/or high temperature resistance coating applications.

Waterborne Systems Emulsions and Dispersions 184 – 204 5,000 – 1,0000 58 APAC, EMEAI, LAA, NAA
D.E.R.™ 917

Emulsion of a standard bisphenol-A liquid epoxy resin, similar to D.E.R. 331™ epoxy resin, in water. 100% VOC free. Designed for civil engineering applications requiring improved crosslink density, solvent resistance and hardness. Also suitable as co-reactant in other aqueous systems.

Waterborne Systems Emulsions and Dispersions 193 – 204 3,000 – 9,000 64 APAC, EMEAI, LAA, NAA
DLVE 18

Low viscosity liquid epoxy resin modified with a Cycloaliphatic polyglycidyl ether for high solids coating formulations with ultra low volatile organic compound (VOC) emissions and ease of application. Excellent corrosion protection and chemical resistance. Can be cured with multiple types of curing agents (hardeners)

DLVE™ & DLVNE™, Liquid Epoxy Resins Low Viscosity Epoxy Resins 160 – 175 400 – 1,000 100 APAC, EMEAI, LAA, NAA
DLVE 19

Low viscosity epoxy resin modified with a Cycloaliphatic polyglycidyl ether for high solids coating formulations with low volatile organic compound (VOC) emissions, excellent application, corrosion and chemical resistance. Can be cured with multiple types of curing agents (hardeners)

DLVE™ & DLVNE™, Liquid Epoxy Resins Low Viscosity Epoxy Resins 185 – 200 2,600 – 4,200 100 APAC, EMEAI, LAA, NAA
DLVE 52

Ultra Low viscosity epoxy resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) for high solids coating formulations with low volatile organic compound (VOC) emissions, excellent application, corrosion and chemical resistance. This resin is more hydrophobic and can provide better surface wetting. Can be cured with multiple types of curing agents (hardeners)

DLVE™ & DLVNE™, Liquid Epoxy Resins Low Viscosity Epoxy Resins 165 – 180 350 – 550 100 APAC, EMEAI, LAA, NAA
DLVNE 59

Low viscosity Novolac resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) for high solids coating formulations with low volatile organic compound (VOC) emissions. Balance of properties similar to solvent borne Novolac.

DLVE™ & DLVNE™ Low Viscosity Epoxy Novolac Resins 160 – 175 2,000 – 4,000 100 APAC, EMEAI, LAA, NAA
DLVNE 59

Low viscosity Novolac resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) for high solids coating formulations with low volatile organic compound (VOC) emissions. Balance of properties similar to solvent borne Novolac.

Epoxy Novolac Resins Low Viscosity Epoxy Novolac Resins 160 – 175 2,000 – 4,000 100 APAC, EMEAI, LAA, NAA
DLVNE 60

Low viscosity Novolac resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) that facilitate high solids coating formulations with low volatile organic compound (VOC) emissions, improved application, strong chemical and thermal resistance.

DLVE™ & DLVNE™ Low Viscosity Epoxy Novolac Resins 166 – 176 1,100 – 1,900 (1) 100 APAC, EMEAI, LAA, NAA 1 @ 51.7 °C
DLVNE 60

Low viscosity Novolac resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) that facilitate high solids coating formulations with low volatile organic compound (VOC) emissions, improved application, strong chemical and thermal resistance.

Epoxy Novolac Resins Low Viscosity Epoxy Novolac Resins 166 – 176 1,100 – 1,900 (1) 100 APAC, EMEAI, LAA, NAA 1 @ 51.7 °C
DLVNE 61

Medium low viscosity Novolac resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) that facilitate high solids coating formulations with low volatile organic compound (VOC) emissions, improved application, strong chemical and thermal resistance.

DLVE™ & DLVNE™ Low Viscosity Epoxy Novolac Resins 155 – 170 4,500 – 6,500 100 APAC, EMEAI, LAA, NAA
DLVNE 61

Medium low viscosity Novolac resin modified with a Cycloaliphatic polyglycidyl ether (free of any organic solvent) that facilitate high solids coating formulations with low volatile organic compound (VOC) emissions, improved application, strong chemical and thermal resistance.

Epoxy Novolac Resins Low Viscosity Epoxy Novolac Resins 155 – 170 4,500 – 6,500 100 APAC, EMEAI, LAA, NAA
FORTEGRA™ 100

Low viscosity toughening agent designed for use in amine or anhydride curing epoxy binder systems.

Epoxy Toughening / Flexibilizing Solutions Epoxy Toughening Agents N/A 3,000 – 4,000 APAC, LAA, NAA
FORTEGRA™ 102

Toughened bisphenol-A liquid epoxy resin master-batch (50 wt%). Allows easy formulation into other liquid epoxy binder systems for composite as well as coating applications

Epoxy Toughening / Flexibilizing Solutions Toughened Epoxy Resins 345 – 374 4,000 – 8,000 LAA, NAA
FORTEGRA™ 104

Specialty 4-type solid epoxy resin with improved toughness and impact resistance designed for fusion bonded epoxy abrasion resistant overcoats.

Epoxy Toughening / Flexibilizing Solutions Toughened Epoxy Resins 960 – 1,060 4,500 – 9,500 (1) NA APAC, EMEAI, LAA, NAA (1) Melt viscosity at 150 ᵒC
FORTEGRA™ 201

Elastomer-modified epoxy functional adduct designed to improve toughness of epoxy systems with minimal impact on thermo-mechanical properties. Offers improved fatigue resistance, thermal shock resistance, impact resistance, and peel and shear strength.

Epoxy Toughening / Flexibilizing Solutions Toughened Epoxy Resins 325 – 360 26,000 – 46,000 LAA, NAA
FORTEGRA™ 202

Low viscosity toughener based on innovative technology. Imparts adhesion, impact resistance and anticorrosion resistance via nanometer size phase separation in curing matrix.

Epoxy Toughening / Flexibilizing Solutions Toughened Epoxy Resins N/A 4,500 – 8,000 APAC
FORTEGRA™ 301

Toughened liquid epoxy resin with core shell rubber particles. Offers improved toughness in coating and composite applications.

Epoxy Toughening / Flexibilizing Solutions Toughened Epoxy Resins 200 – 225 2,700 – 3,500 (2) (2) @ 50 °C
FORTEGRA™ 304

Specialty solid resin designed to improve flexibility and impact resistance of fusion bonded epoxy coatings

Epoxy Toughening / Flexibilizing Solutions Toughened Epoxy Resins 920 – 1,090 8,000 – 23,000 (1) 105 – 115 APAC, EMEAI, LAA, NAA 1 @ 150 °C
FORTEGRA™ 310

Specialty resin designed to improve flexibility and impact resistance of fusion bonded epoxy coatings with high glass transition temperature ( up to 160 °C)

Epoxy Toughening / Flexibilizing Solutions Toughened Epoxy Resins 400 – 450 5,000 – 15,000 (1) 105 – 117 APAC, EMEAI, LAA, NAA
FORTEGRA™ 352

A stable dispersion of preformed novel Core Shell Rubber (CSR) particles in a bisphenol A liquid epoxy resin containing 33wt% of the CSR.

Epoxy Toughening / Flexibilizing Solutions Toughened Epoxy Resins 248 – 268 17,000 – 23,000 (2) LAA, NAA (2) @ 50 °C
LITESTONE™ 1100E / 1101H

Hand-/Wet-Layup Epoxy system; fast cure

LITESTONE™ Composite Systems Epoxy Composites 100/31 (1) NA 50 APAC, EMEAI, LAA, NAA (1) Mix ratio (by weight) in PHR, (2) Mix viscosity
LITESTONE™ 1100E / 1103H

Hand-/Wet-Layup Epoxy system; long pot life

LITESTONE™ Composite Systems Epoxy Composites 100/31 (1) NA 500 APAC, EMEAI, NAA (1) Mix ratio (by weight) in PHR, (2) Mix viscosity
LITESTONE™ 1500E / 1501H

Standard Resin Infusion Epoxy system; fast cure

LITESTONE™ Composite Systems Epoxy Composites 100/32 (1) 420 (2) 60 EMEAI, LAA (1) Mix ratio in PHR, (2) Mix viscosity
LITESTONE™ 1500E / 1503H

Standard Resin Infusion Epoxy system; long pot life

LITESTONE™ Composite Systems Epoxy Composites 100/32 (1) 330 (2) 300 APAC, EMEAI, LAA, NAA (1) Mixing ratio in PHR, (2) Mix viscosity
LITESTONE™ 1550E / 1553H

Advanced Resin Infusion Epoxy system; due to excellent wetting and low viscosity especially recommended for Carbon Fiber Infusion; long pot life

LITESTONE™ Composite Systems Epoxy Composites 100/31 (1) 220 (2) 650 APAC, EMEAI, LAA, NAA (1) Mix ratio in PHR, (2) Mix viscosity
LITESTONE™ 1900E / 1901H

Mold Building/Tooling System; fast cure

LITESTONE™ Composite Systems Epoxy Composites 100/28 (1) 415 (3) NA EMEAI (1) Mixing ratio in PHR, (3) Mix viscosity @ 30 ᵒC
LITESTONE™ 1900E / 1903H

Mold Building/Tooling System; long pot life

LITESTONE™ Composite Systems Epoxy Composites 22 (1) 300 (3) NA EMEAI (1) Mixing ratio in PHR, (3) Mix viscosity @ 30 ᵒC
LITESTONE™ 2130E / 2131H

Anhydride curing system developed especially for Filament Winding applications; Tg ~125°C

LITESTONE™ Composite Systems Epoxy Composites 93 – 98 (1) 470 (2) > 24 hours EMEAI (1) Mix ratio in PHR, (2) Mix viscosity
LITESTONE™ 2130E / 2142H

Toughened Anhydride curing system developed especially for Filament Winding applications; Tg ~115°C

LITESTONE™ Composite Systems Epoxy Composites 100/95 – 100 (1) 500 (2) > 12 hours APAC, EMEAI, LAA, NAA (1) Mix ratio in PHR, (2) Mix viscosity
LITESTONE™ 2210E / 2212H

Toughened anhydride curing system developed especially for Filament Winding applications; Tg ~210°C

LITESTONE™ Composite Systems Epoxy Composites 125 (1) 1000 (2) 12 hours EMEAI (1) Mixing ratio in PHR, (2) Mix viscosity
Litestone™ 3100E / 3101H

Anhydride curing system developed especially for Pultrusion applications; Tg ~120°C

LITESTONE™ Composite Systems Epoxy Composites NA NA NA EMEAI (1) Mixing ratio in PHR,
(2) Mix viscosity
Litestone™ 3100E / 3103H

Anhydride curing system developed especially for Pultrusion applications; Tg ~120°C

LITESTONE™ Composite Systems Epoxy Composites 100 (1) 1200 (2) > 12 hours EMEAI (1) Mixing ratio in PHR,
(2) Mix viscosity
Litestone™ 3100E / 3122H

Anhydride curing system developed especially for Pultrusion applications; Tg ~140°C

LITESTONE™ Composite Systems Epoxy Composites 103 (1) 850 (2) > 24 hours EMEAI (1) Mixing ratio in PHR,
(2) Mix viscosity
Litestone™ 3170E / 3172H

Anhydride curing system developed especially for Pultrusion applications; Tg ~170°C

LITESTONE™ Composite Systems Epoxy Composites 114 (1) 750 (2) > 24 hours EMEAI (1) Mixing ratio in PHR,
(2) Mix viscosity
XZ 92573.00

Liquid epoxy resin for autmotive applications

Liquid Epoxy Resins Modified Bisphenol A Liquid Epoxy Resins 335  – 370 2,400 – 4,000 100 EMEAI
XZ 97103.00

Low molecular weight high Tg epoxy resin modified with oxazolidone to improve tougness. To be used as an adhesion promoter as well.

Epoxy Toughening / Flexibilizing Solutions Toughened Epoxy Resins 280 – 305 500 – 2,500 74 – 76 NAA