Our LITESTONE® System for Composites offers the reliability, protection and performance you need, backed by the local customer support Only Olin can provide, virtually anywhere in the world.
Discover more about Olin Epoxy’s Composite Systems
| Product Name & Description | Type | EEW Based on solids (g/eq) | Viscosity @25°C (mPa.s) | Pot Life Min. | Regional Availability
APAC - Asia, Pacific
EMEAI - Europe, Middle East, Africa, India LAA - Latin America Area NAA - North America Area |
Footnote |
|---|---|---|---|---|---|---|
|
LITESTONE® 1100E / 1101H
Hand-/Wet-Layup Epoxy system; fast cure |
Epoxy Composites | 100/31 (1) | NA | 50 | EMEAI, LAA, NAA | (1) Mix ratio (by weight) in PHR, (2) Mix viscosity |
|
LITESTONE® 1100E / 1103H
Hand-/Wet-Layup Epoxy system; long pot life |
Epoxy Composites | 100/31 (1) | NA | 500 | EMEAI, NAA | (1) Mix ratio (by weight) in PHR, (2) Mix viscosity |
|
LITESTONE® 1500E / 1501H
Standard Resin Infusion Epoxy system; fast cure |
Epoxy Composites | 100/32 (1) | 420 (2) | 60 | EMEAI, LAA | (1) Mix ratio in PHR, (2) Mix viscosity |
|
LITESTONE® 1500E / 1503H
Standard Resin Infusion Epoxy system; long pot life |
Epoxy Composites | 100/32 (1) | 330 (2) | 300 | LAA, NAA | (1) Mixing ratio in PHR, (2) Mix viscosity |
|
LITESTONE® 1550E / 1553H
Advanced Resin Infusion Epoxy system; due to excellent wetting and low viscosity especially recommended for Carbon Fiber Infusion; long pot life |
Epoxy Composites | 100/31 (1) | 220 (2) | 650 | LAA, NAA | (1) Mix ratio in PHR, (2) Mix viscosity |
|
LITESTONE® 1900E / 1901H
Mold Building/Tooling System; fast cure |
Epoxy Composites | 100/28 (1) | 415 (3) | NA | – | (1) Mixing ratio in PHR, (3) Mix viscosity @ 30 ᵒC |
|
LITESTONE® 1900E / 1903H
Mold Building/Tooling System; long pot life |
Epoxy Composites | 22 (1) | 300 (3) | NA | – | (1) Mixing ratio in PHR, (3) Mix viscosity @ 30 ᵒC |
|
LITESTONE® 2050E
Higher viscosity Filament Winding Resin for tuning system viscosity |
Epoxy Composites | 180 | 8500 | NA | EMEAI, LAA, NAA | – |
|
LITESTONE® 2100E / 2105H
Benchmark amine system for filament winding. Good balance of potlife and reactivity. |
Epoxy Composites | 100/30 (1) | 450 (2) | 540 | EMEAI, LAA, NAA | (1) mix ratio by weight in PHR, (2) mix viscosity |
|
LITESTONE® 2100E / 2117H
Toughened amine system. Offers a long pot life combined with state of the art toughening technology |
Epoxy Composites | 100/29 (1) | 400 (2) | 400 | EMEAI, LAA, NAA | (1) mix ratio by weight in PHR, (2) mix viscosity |
|
LITESTONE® 2130E / 2131H
Anhydride curing system developed especially for Filament Winding applications; Tg ~125°C |
Epoxy Composites | 93 – 98 (1) | 470 (2) | > 24 hours | EMEAI | (1) Mix ratio in PHR, (2) Mix viscosity |
|
LITESTONE® 2130E / 2142H
Toughened Anhydride curing system developed especially for Filament Winding applications; Tg ~115°C |
Epoxy Composites | 100/95 – 100 (1) | 500 (2) | > 12 hours | APAC, EMEAI, LAA, NAA | (1) Mix ratio in PHR, (2) Mix viscosity |
|
LITESTONE® 2210E / 2212H
Toughened anhydride curing system developed especially for Filament Winding applications; Tg ~210°C |
Epoxy Composites | 125 (1) | 1000 (2) | 12 hours | – | (1) Mixing ratio in PHR, (2) Mix viscosity |
|
LITESTONE® 3100E / 3101H
Anhydride curing system developed especially for Pultrusion applications; Tg ~120°C |
Epoxy Composites | NA | NA | NA | – | (1) Mixing ratio in PHR, (2) Mix viscosity |
|
LITESTONE® 6130E
Ready to use resin for hot melt prepreg formulations |
Epoxy Composites | NA | 12500 (1) | NA | EMEAI, LAA, NAA | (1) at 70°C |
|
LITESTONE® VF 4330 / VF 4335
Standard system for HP-RTM and LCM. Offers extra fast curing time combined with an excellent latency and good surface quality potential. Formerly known as Voraforce 3300 series |
Epoxy Composites | 100/21 (1) | 8000 (2) | NA | EMEAI, LAA, NAA | (1) mix ratio by weight in PHR, (2) mix viscosity |
|
LITESTONE® 200C
Catalyst for fine tuning reactivity and adjusting line speed |
Epoxy Composites | NA | 200 | NA | EMEAI, LAA, NAA | – |
|
LITESTONE® 2100E / 2142H
Toughened Anhydride curing system developed especially for Filament Winding applications; Tg ~120°C |
Epoxy Composites | 100/97-111 (1) | 500-800 (2) | > 2880 | LAA, NAA | (1) Mixing ratio (by weight) in PHR, (2) Mix viscosity |
|
LITESTONE® 3100E / 3102H
Industry benchmark for Epoxy Pultrusion. Optimally trimmed to combine line speed with process robustness and surface quality |
Epoxy Composites | 100/105 (1) | 1500 (2) | 720 | EMEAI, LAA, NAA | (1) mix ratio by weight in PHR, (2) mix viscosity |
|
LITESTONE® 3100E / 3103H
Anhydride curing system developed especially for Pultrusion applications; Tg ~120°C |
Epoxy Composites | 100 (1) | 1200 (2) | > 12 hours | – | (1) Mixing ratio in PHR, (2) Mix viscosity |
|
LITESTONE® 3100E / 3122H
Anhydride curing system developed especially for Pultrusion applications; Tg ~140°C |
Epoxy Composites | 103 (1) | 850 (2) | > 24 hours | – | (1) Mixing ratio in PHR, (2) Mix viscosity |
|
LITESTONE® 3170E / 3172H
Anhydride curing system developed especially for Pultrusion applications; Tg ~170°C |
Epoxy Composites | 114 (1) | 750 (2) | > 24 hours | – | (1) Mixing ratio in PHR, (2) Mix viscosity |
|
LITESTONE® 3200E / 3101H
Industry benchmark for pullwinding. The two-component formulation, compared with conventional three component systems, enables a leaner process |
Epoxy Composites | 100/92 (1) | 500 (2) | >1440 | EMEAI, LAA, NAA | (1) mix ratio by weight in PHR, (2) mix viscosity |
|
LITESTONE® 3400E / 3102H
Low viscosity version of our Industry benchmark for Epoxy Pultrusion. Optimally trimmed to combine line speed with process robustness and surface quality |
Epoxy Composites | 100/105 (1) | 800 (2) | 720 | EMEAI, LAA, NAA | (1) mix ratio by weight in PHR, (2) mix viscosity |
|
LITESTONE® VF 4530 / VF 4535
Standard system for HP-RTM and LCM. Offers ultra fast curing time combined with an excellent latency and good demouldability. Formerly known as Voraforce 5300 series |
Epoxy Composites | 100/16 (1) | 8000 (2) | NA | EMEAI, LAA, NAA | (1) mix ratio by weight in PHR, (2) mix viscosity |